Trench gate metal oxide semiconductor field effect transistor and fabricating method thereof

ABSTRACT

A trench gate metal oxide semiconductor field effect transistor includes a substrate and a gate. The substrate has a trench. The trench is extended downwardly from a surface of the substrate. The gate includes an insertion portion and a symmetrical protrusion portion. The insertion portion is embedded in the trench. The symmetrical protrusion portion is symmetrically protruded over the surface of the substrate.

FIELD OF THE INVENTION

The present invention relates to a semiconductor device and afabricating method thereof, and more particularly to a trench gate metaloxide semiconductor field effect transistor and a fabricating methodthereof.

BACKGROUND OF THE INVENTION

A conventional trench gate metal oxide semiconductor field effecttransistor comprises a gate structure, which is disposed within atrench. For fabricating the conventional trench gate metal oxidesemiconductor field effect transistor, a trench is firstly formed in asemiconductor substrate, and then a gate dielectric layer is formed on asidewall of the trench by thermal oxidation. Then, a polysiliconsemiconductor material is filled into the trench. After a planarizationprocess is performed, a polysilicon gate is formed in the trench.

Recently, since the integrated circuit becomes more complicated, thefeature size and wiring space of the semiconductor device are graduallydecreased, and the size of the polysilicon gate is reduced. After thepolysilicon gate is formed, a metal contact plug is formed on thepolysilicon gate in the subsequent process. As known, the size reductionof the polysilicon gate may result in misalignment between thepolysilicon gate and the metal contact plug. If the metal contact plugis deviated because of misalignment, the metal contact plug and theneighboring circuits may be suffered from charge breakdown.

Therefore, there is a need of providing an improved trench gate metaloxide semiconductor field effect transistor and a fabricating methodthereof in order to obviate the drawbacks encountered from the priorart.

SUMMARY OF THE INVENTION

In accordance with an aspect, the present invention provides a trenchgate metal oxide semiconductor field effect transistor. The trench gatemetal oxide semiconductor field effect transistor includes a substrateand a gate. The substrate has a trench. The trench is extendeddownwardly from a surface of the substrate. The gate includes aninsertion portion and a symmetrical protrusion portion. The insertionportion is embedded in the trench. The symmetrical protrusion portion issymmetrically protruded over the surface of the substrate.

In an embodiment, the symmetrical protrusion portion is wider than thetrench.

In an embodiment, the gate is a T-shaped gate, which is symmetrical withrespect to a central line of the trench.

In an embodiment, the trench has a width smaller than or equal to 0.8 μmand a depth of about 1.6 μm.

In an embodiment, the trench gate metal oxide semiconductor field effecttransistor includes a dielectric material layer and a contact plug. Thedielectric material layer is disposed over the surface of the substrateand the gate. The contact plug is penetrated through the dielectricmaterial layer and electrically contacted with the symmetricalprotrusion portion of the gate.

In an embodiment, the trench gate metal oxide semiconductor field effecttransistor includes a first-conductive doped region, a second-conductivedoped region, a gate dielectric layer, and a source region. Thefirst-conductive doped region is formed in the substrate. Thesecond-conductive doped region is formed in the substrate. A P/Njunction is formed between the first-conductive doped region and thesecond-conductive doped region. The trench is extended downwardly fromthe surface of the trench, penetrated through the first-conductive dopedregion and the P/N junction, and inserted into the second-conductivedoped region. The gate dielectric layer is formed on a sidewall of thetrench. The source region is formed in the substrate and located besidethe gate dielectric layer.

In an embodiment, the first-conductive doped region is a P-type bodyregion, and the second-conductive doped region is an N-type well region.

In an embodiment, the trench gate metal oxide semiconductor field effecttransistor further includes an N-type buried layer, which is disposedunder the second-conductive doped region.

In an embodiment, the source region is an N-type well region, and thesource region is extended from the surface of the substrate into thefirst-conductive doped region.

In accordance with an aspect, the present invention provides a methodfor fabricating a trench gate metal oxide semiconductor field effecttransistor. The method includes the following steps. Firstly, asubstrate is provided. Then, a hard mask layer is formed on thesubstrate. Then, an etching process is performed to remove a part of thehard mask layer and form a trench in the substrate. Then, an etchingback process is performed to remove a part of the hard mask layer. Then,a conductive layer is formed on the hard mask layer and filled into thetrench. Then, a planarization process is performed to remove theconductive layer by using the hard mask layer as a stop layer.

In an embodiment, before the hard mask layer is formed, the methodfurther includes a step of forming a pad silicon oxide layer on thesubstrate.

In an embodiment, after the hard mask layer is formed, the methodfurther includes a step of forming a sacrificial layer on the hard masklayer.

In an embodiment, before the conductive layer is formed, the methodfurther comprises a step of forming a gate dielectric layer on asidewall of the trench by a thermal oxidation process.

In an embodiment, the hard mask layer is a silicon oxide layer or asilicon nitride layer.

BRIEF DESCRIPTION OF THE DRAWINGS

The above objects and advantages of the present invention will becomemore readily apparent to those ordinarily skilled in the art afterreviewing the following detailed description and accompanying drawings,in which:

FIGS. 1A˜1F are schematic cross-sectional views illustrating a methodfor fabricating a trench gate metal oxide semiconductor field effecttransistor according to an embodiment of the present invention;

FIGS. 2A˜2E are schematic cross-sectional views illustrating a methodfor fabricating a trench gate metal oxide semiconductor field effecttransistor according to another embodiment of the present invention; and

FIG. 3 is a schematic cross-sectional view illustrating an optional stepof the method for fabricating the trench gate metal oxide semiconductorfield effect transistor of the present invention.

DETAILED DESCRIPTION OF PREFERRED EMBODIMENTS

The present invention will now be described more specifically withreference to the following embodiments. It is to be noted that thefollowing descriptions of preferred embodiments of this invention arepresented herein for purpose of illustration and description only. It isnot intended to be exhaustive or to be limited to the precise formdisclosed.

FIGS. 1A˜1F are schematic cross-sectional views illustrating a methodfor fabricating a trench gate metal oxide semiconductor field effecttransistor according to an embodiment of the present invention. Themethod for fabricating the trench gate metal oxide semiconductor fieldeffect transistor 100 comprises the following steps.

Firstly, as shown in FIG. 1A, a substrate 101 is provided. In anembodiment, the substrate 101 is a silicon substrate. In addition, thesubstrate 101 comprises a first-conductive doped region 101 a, asecond-conductive doped region 101 b, a source region 120, and asecond-conductive deep well region 101 c.

The first-conductive doped region 101 a, the second-conductive dopedregion 101 b, the source region 120 and the second-conductive deep wellregion 101 c are formed in the substrate 101 by a plurality of ionimplantation processes. The second-conductive doped region 101 b isformed in the substrate 101. The first-conductive doped region 101 a isdisposed over the second-conductive doped region 101 b, and extendeddownwardly from a surface 101 d of the substrate 101 to be contactedwith the second-conductive doped region 101 b. Consequently, a P/Njunction 102 is formed between the first-conductive doped region 101 aand the second-conductive doped region 101 b. The source region 120 isextended downwardly from the surface 101 d of the substrate 101, andformed in the first-conductive doped region 101 a. The second-conductivedeep well region 101 c is formed in the substrate 101, and extendeddownwardly from the surface 101 d of the substrate 101, serving as thedrain of the trench gate metal oxide semiconductor field effecttransistor 100. Moreover, the second-conductive deep well region 101 cis contacted with the second-conductive doped region 101 b. Furthermore,a buried layer 119 with the same conductivity as the second-conductivedoped region 101 b is disposed under the second-conductive doped region101 b.

In this embodiment, the second-conductive doped region 101 b is anN-type well region with a lower dopant concentration. Thefirst-conductive doped region 101 a is a P-type body region. The sourceregion 120 is an N-type well region with a higher dopant concentration.The second-conductive deep well region 101 c is an N-type deep wellregion. The second-conductive deep well region 101 c is isolated fromthe first-conductive doped region 101 a through a shallow trenchisolation structure 103. The buried layer 119 is an N-type doped regionwith a higher dopant concentration. The buried layer 119 is disposedunder the second-conductive doped region 101 b and contacted with thesecond-conductive deep well region 101 c. Preferably, an N-type wellregion 101 e with a dopant concentration greater than that of the N-type(second-conductive) deep well region 101 c, maybe formed in the N-type(second-conductive) deep well region 101 c, and extended downwardly fromthe surface 101 d of the substrate 101.

Then, as shown in FIG. 1B, by film deposition processes or any othersuitable processes, a pad silicon oxide layer 104, a hard mask layer 105and a patterned photoresist layer 106 are formed on the surface 101 d ofthe substrate 101 to cover the second-conductive deep well region 101 c,the source region 120 and the first-conductive doped region 101 a. Forexample, the hard mask layer 105 is made of silicon nitride.Alternatively, the hard mask layer 105 may be made of silicon oxide.

Then, as shown in FIG. 1C, by using the patterned photoresist layer 106as an etching mask, an etching process 107 is performed to remove a partof the hard mask layer 105, a part of the pad silicon oxide layer 104and a part of the substrate 101. Consequently, a trench 108 is formed inthe substrate 101. The trench 108 is extended downwardly from thesurface 101 d of the substrate 101, penetrated through the source region120, and extended into the second-conductive doped region 101 b. Forexample, the etching process 107 is a dry etching process. The trench108 has a width smaller than or equal to 0.8 μm and a depth of about 1.6μm.

After the patterned photoresist layer 106 and the remaining hard masklayer 105 are removed, a thermal oxidation process is performed to forma gate dielectric layer 109 on a sidewall 108 a of the trench 108 (seeFIG. 1D). Then, a conductive layer, preferably a polysilicon layer 110,is formed on the pad silicon oxide layer 104, and filled into the trench108. Then, a planarization process 111 (e.g. a chemical mechanicalpolishing process) is performed to partially remove the polysiliconlayer 110.

After the planarization process 111 is performed, a patternedphotoresist layer 112 is formed on the polysilicon layer 110. By usingthe pad silicon oxide layer 104 as an etch stop layer, another etchingprocess 113 is performed to remove a part of the planarized polysiliconlayer 110. Consequently, a T-shaped portion of the planarizedpolysilicon layer 110 is remained and serves as a T-shaped polysilicongate 114 of the trench gate metal oxide semiconductor field effecttransistor 100(see FIG. 1E). The T-shaped polysilicon gate 114 comprisesan insertion portion 114 a and a protrusion portion 114 b. The insertionportion 114 a is embedded in the trench 108. The protrusion portion 114b is protruded over the surface 101 d of the substrate 101 andexternally and transversely extended from a central line 108 b of thetrench 108.

Then, a metal interconnection process is performed. Consequently, adielectric material layer 117 is firstly formed over the surface 101 dof the substrate 101 and the polysilicon gate 114, and then a pluralityof metal contact plugs 118 are formed in the dielectric material layer117. Meanwhile, the trench gate metal oxide semiconductor field effecttransistor 100 is produced. The resulting structure of the trench gatemetal oxide semiconductor field effect transistor 100 is shown in FIG.1F.

Please refer to FIG. 1F again. In the T-shaped polysilicon gate 114, thetransversely-extending width of the protrusion portion 114 b is greaterthan the width of the insertion portion 114 a. Consequently, theprotrusion portion 114 b can provide a larger process window for thesubsequently forming of the metal contact plug 118 on the polysilicongate 114.

However, the above-mentioned method for fabricating the trench gatemetal oxide semiconductor field effect transistor 100 still has somedrawbacks. For example, since two photolithography and etching processesare required to form the polysilicon gate 114, every misalignment errorof the photomask may further decrease the alignment accuracy. Moreover,during the performing of the etching process 113, the surface 101 d ofthe substrate 101 is still completely covered by the planarizedpolysilicon layer 110. Since the alignment mark for the etching process113 is possibly hindered by the planarized polysilicon layer 110, themisalignment error of the photomask is thereby increased. Due to themisalignment error of the photomask, the protrusion portion 114 b of thepolysilicon gate 114 may be unexpectedly and asymmetrically extended inthe transverse direction. If the (alignment) process errors in theprocess of forming the metal contact plug 118 are taken intoconsideration, the total cumulative misalignment error of thesemiconductor device is very large. Under this circumstance, the metalcontact plug 118 and the neighboring circuits may be suffered fromcharge breakdown.

For solving the above drawbacks, the method of forming the polysilicongate 114 needs to be further improved.

FIGS. 2A˜2E are schematic cross-sectional views illustrating a methodfor fabricating a trench gate metal oxide semiconductor field effecttransistor according to another embodiment of the present invention. Themethod for fabricating the trench gate metal oxide semiconductor fieldeffect transistor 200 comprises the following steps.

Firstly, the steps as shown in FIGS. 1A, 1B and 1C are sequentiallyperformed. After the trench 108 is formed (see FIG. 1C), the remaininghard mask layer 105 is not removed immediately. On the other hand, asshown in FIG. 2A according to the embodiment of present invention, afterthe patterned photoresist layer 106 is removed, an etching back process215 is performed to remove the patterned photoresist layer 106 and apart of the hard mask layer 105, and a part of the pad silicon oxidelayer 104 at an entrance 108 c of the trench 108 that is exposed. In anembodiment, the hard mask layer 105 is made of silicon nitride, and theetching back process 215 is a wet etching process by using a phosphoricacid solution as an etchant solution to remove a part of the hard masklayer 105. Alternatively, in another embodiment, the hard mask layer 105is made of silicon dioxide, and the etching back process 215 is a wetetching process by using a buffer oxide etcher (BOE) solution as anetchant solution to remove a part of the hard mask layer 105.

Furthermore, for improved control of the etching back process 215,before the patterned photoresist layer 106 is formed, another silicondioxide layer 316 may be optionally formed on the hard mask layer 105(see FIG. 3). The silicon dioxide layer 316 is served as a sacrificiallayer for the etching back process 215 in order to adjust the etchingdepth and range of the etching back process 215.

Then, a thermal oxidation process is performed to form a gate dielectriclayer 109 on a sidewall 108 a of the trench 108 (see FIG. 2B). Then, asshown in FIG. 2C, a polysilicon layer 110 is formed on the remaininghard mask layer 105 and the exposed pad silicon oxide layer 104, andfilled into the trench 108.

Then, a planarization process 111 (e.g. a chemical mechanical polishingprocess) is performed to remove the polysilicon layer 110 by using thehard mask layer 105 as a polish stop layer. After the remaining hardmask layer 105 is removed, a T-shaped polysilicon gate 214 is formed(see FIG. 2D). The T-shaped polysilicon gate 214 is configuredsymmetrical with respect to a central line 108 b of the trench 108. TheT-shaped polysilicon gate 214 comprises an insertion portion 214 a and asymmetrical protrusion portion 214 b. The insertion portion 214 a isembedded in the trench 108. The symmetrical protrusion portion 214 b isprotruded over the surface 101 d of the substrate 101, symmetrical withrespect to the central line 108 b of the trench 108, and externally andtransversely extended from the central line 108 b of the trench 108.

Then, a metal interconnection process is performed. Consequently, adielectric material layer 117 is firstly formed over the surface 101 dof the substrate 101 and the polysilicon gate 214, and then a pluralityof metal contact plugs 118 are formed in the dielectric material layer117. Meanwhile, the trench gate metal oxide semiconductor field effecttransistor 200 is produced. The resulting structure of the trench gatemetal oxide semiconductor field effect transistor 200 is shown in FIG.2E.

From the above discussions, the structure of the polysilicon gate 214 ofthe trench gate metal oxide semiconductor field effect transistor 200 isimproved in comparison to the trench gate MOSFET 100 shown in FIGS.1A-1F. For forming the polysilicon gate 214, a part of the hard masklayer 105 at the entrance 108 c of the trench 108 is firstly removed byan etching back process (e.g. an anisotropic etching process) (see FIG.2A), then the polysilicon layer 110 is filled into the trench 108, andfinally a planarization process is performed. Consequently, thesymmetrical protrusion portion 214 b of the polysilicon gate 214 can besymmetrically configured with respect to the central line 108 b of thetrench 108 and transversely extended from the central line 108 b of thetrench 108 (see FIG. 2D). The symmetrical protrusion portion 114 b canprovide a larger process window for subsequently forming of the metalcontact plug 118 on the polysilicon gate 214. Consequently, even if thefeature size of the semiconductor device is shrunken down, themisalignment error thereof will be largely reduced.

Moreover, according to the embodiments of the fabricating method of thepresent invention, only a single photolithography and etching process issufficient to form a polysilicon gate, instead of requiring twophotolithography and etching processes to form the same. Consequently,the fabricating method of the present invention is simplified, thephotomask number is reduced, and the misalignment error of thesemiconductor device is largely reduced. Since the misalignment error islargely reduced, the symmetrical protrusion portion of the polysilicongate is no longer unexpectedly and asymmetrically extended in thetransverse direction, and the total cumulative misalignment error of thesemiconductor device is reduced.

From the above discussions, the present invention provides a trench gatemetal oxide semiconductor field effect transistor and a fabricatingmethod thereof. The fabricating method comprises the following steps.Firstly, a substrate is provided. Then, a hard mask layer is formed onthe substrate. Then, an etching process is performed to remove a part ofthe hard mask layer and form a trench in the substrate. Then, an etchingback process is performed to remove a part of the hard mask layer. Then,a polysilicon layer is formed on the hard mask layer and filled into thetrench. Then, by using the hard mask layer as a stop layer, aplanarization process is performed to remove the polysilicon layer.Consequently, a polysilicon gate with the symmetrical protrusion portionis formed.

The symmetrical protrusion portion of the polysilicon gate can provide alarger process window for subsequently forming the metal contact plug onthe polysilicon gate. Consequently, even if the feature size of thedevice is shrunken down, the misalignment error will be largely reduced.

From the above descriptions, the symmetrical protrusion portion of thepolysilicon gate is formed by etching back the hard mask layer to widenthe entrance of the trench and then filling the polysilicon layer.Consequently, it is not necessary to perform an additionalphotolithography and etching process. In other words, the fabricatingmethod of the present invention is simplified and cost-effective. Sinceit is not necessary to repeatedly use the photomask for alignment, theprecision of the alignment between the metal contact plug and thepolysilicon gate is enhanced.

While the invention has been described in terms of what is presentlyconsidered to be the most practical and preferred embodiments, it is tobe understood that the invention needs not be limited to the disclosedembodiment. On the contrary, it is intended to cover variousmodifications and similar arrangements included within the spirit andscope of the appended claims which are to be accorded with the broadestinterpretation so as to encompass all such modifications and similarstructures.

1. A trench gate metal oxide semiconductor field effect transistor,comprising: a substrate having a trench formed therein, wherein thetrench is extended downwardly from a surface of the substrate; and agate comprising an insertion portion and a symmetrical protrusionportion, wherein the insertion portion is embedded in the trench, andthe symmetrical protrusion portion is symmetrically protruded over thesurface of the substrate.
 2. The trench gate metal oxide semiconductorfield effect transistor according to claim 1, wherein the symmetricalprotrusion portion is wider than the trench.
 3. The trench gate metaloxide semiconductor field effect transistor according to claim 1,wherein the gate is a T-shaped gate, which is symmetrical with respectto a central line of the trench.
 4. The trench gate metal oxidesemiconductor field effect transistor according to claim 1, wherein thetrench has a width smaller than or equal to 0.8 μm and a depth of about1.6 μm.
 5. The trench gate metal oxide semiconductor field effecttransistor according to claim 1, further comprising: a dielectricmaterial layer disposed over the surface of the substrate and the gate;and at least one contact plug penetrated through the dielectric materiallayer and electrically contacted with the symmetrical protrusion portionof the gate.
 6. The trench gate metal oxide semiconductor field effecttransistor according to claim 1, further comprising: a first-conductivedoped region formed in the substrate; a second-conductive doped regionformed in the substrate, wherein a P/N junction is formed between thefirst-conductive doped region and the second-conductive doped region,the trench is extended downwardly from the surface of the trench,penetrated through the first-conductive doped region and the P/Njunction, and inserted into the second-conductive doped region; a gatedielectric layer formed on a sidewall of the trench; and a source regionformed in the substrate and located beside the gate dielectric layer. 7.The trench gate metal oxide semiconductor field effect transistoraccording to claim 6, wherein the first-conductive doped region is aP-type body region, and the second-conductive doped region is an N-typewell region.
 8. The trench gate metal oxide semiconductor field effecttransistor according to claim 6, further comprising an N-type buriedlayer, which is disposed under the second-conductive doped region. 9.The trench gate metal oxide semiconductor field effect transistoraccording to claim 6, wherein the source region is an N-type wellregion, and the source region is extended from the surface of thesubstrate into the first-conductive doped region.
 10. A method forfabricating a trench gate metal oxide semiconductor field effecttransistor, the method comprising steps of: providing a substrate;forming a hard mask layer on the substrate; performing an etchingprocess to remove a part of the hard mask layer and forming a trench inthe substrate; performing an etching back process to remove a part ofthe hard mask layer; forming a conductive layer on the hard mask layer,and filling the polysilicon layer into the trench; and performing aplanarization process to remove the conductive layer by using the hardmask layer as a stop layer.
 11. The method according to claim 10,wherein before the hard mask layer is formed, the method furthercomprises a step of forming a pad silicon oxide layer on the substrate.12. The method according to claim 10, wherein after the hard mask layeris formed, the method further comprises a step of forming a sacrificiallayer on the hard mask layer.
 13. The method according to claim 10,wherein before the conductive layer is formed, the method furthercomprises a step of forming a gate dielectric layer on a sidewall of thetrench by a thermal oxidation process.
 14. The method according to claim10, wherein the hard mask layer is a silicon oxide layer or a siliconnitride layer.